Item | Unit | MCPET | MCPOLYCA | ||||||
---|---|---|---|---|---|---|---|---|---|
Base resin | - | Polyethylene terephthalate | Polycarbonate | ||||||
Grade | - | RB | E3 | M4 | P3 | S4 | M4 (0.5mm) |
YN | |
Structure | - | UV-tempered |
UV coating on one side |
Diffusivity improvement formulation |
UV coating on one side |
Diffusivity improvement formulation |
Satin process UV-tempered |
||
Thickness | mm | 0.94 | 0.88 | 1.0 | 0.55 | 0.51 | 0.5 | 0.99 | |
Total reflectivity (Note 1) |
% | 100.1 | 101.7 | 101.1 | 101.7 | 101.3 | 101.1 | 100.2 | |
Diffusing reflectivity (Note 1) | % | 98.8 | 97.9 | 100.8 | 96.9 | 95.7 | 100.8 | 98.3 | |
Surface resistance | Ω | 1012 | 1016 | 1014 | 1016 | 1014 | 1014 | 1017 | |
UL94 | - | HBF | HBF | To be acquired | - | HBF | To be acquired | HBF | |
Ultraviolet light resistance (not for outdoor use) (Note 2) | - | ||||||||
Standard size (width × length) |
mm | 600×1000 600×1200 600×1500 |
600×1200 600×1500 |
600×1200 600×1500 |
650×1200 650×1500 |
600×1200 600×1500 |
600×1200 600×1500 |
700×1500 | |
Forming process | Vacuum forming | - | Not possible | - | Not possible | - | - | - | Possible |
Matched molding forming | - | Possible | - | Possible | - | - | - | Possible | |
Maximum aspect ratio | - | 0.5 | - | 0.3 | - | - | - | 1.0 |
(Note 1) The reflectivity values shown are the relative values compared with barium sulfate at 550 nm.
(Note 2) : Recommended : Depending on the use environment : Not suited for outdoor use
(Note 3) The figures represent reference values and are not guaranteed values.